HRVATSKO DRUŠTVO ZA ZAŠTITU MATERIJALA CROATIAN SOCIETY FOR MATERIALS PROTECTION
|
|
|
12. SAVJETOVANJE O ZAŠTITI MATERIJALA I INDUSTRIJSKOM FINIŠU 12th CONFERENCE ON MATERIALS PROTECTION AND INDUSTRIAL FINISHING
|
|
| Autor(i)/Author(s):
Jadranka Malina, Ivica Šešerin
|
|
|
UTJECAJ VODIKOVE DEPOLARIZACIJE NA MEHANIČKA SVOJSTVA FERITNO-PERLITNIH ČELIKA |
THE INFLUENCE OF HYDROGEN DEPOLARIZATION ON MECHANICAL PROPERTIES OF FERRITE-PEARLITE STEELS |
| SAŽETAK Uzorci komercijalnih čeličnih cijevi (casing i spojnica) bili su "nabijani" vodikom pomoću dvije različite metode. Elektrolitičko punjenje tijekom katodne polarizacije u H2SO4 ukazalo je da vodik apsorbiran u zamkama mikrostrukture uzrokuje značajnu degradaciju mehaničkih svojstava vezanih s duktilnošću materijala. Punjenje vodikom u NACE-otopini zasićenoj s H2S dalo je uvid u stepeničastu morfologiju pukotina nastalih zbog Haps. Fraktografske analize pokazale su razliku u izgledu prijelomnih povrsina: dok je žilavi prijelom bio karakterističan za vodikom netretirani materijal, nakon punjenja s vodikom prevladavao je krhki kalavi prijelom interkristalnog ili transkristalnog tipa. KLJUČNE RIJEČI niskolegirani čelik, vodikova krhkost, mehanička svojstva, stepeničasto raspucavanje |
SUMMARY
The samples of commercial tubes (casing and coupling) were charged with hydrogen by two different methods. Electrolytic charging during the chatodic polarization in H2SO4 revealed that hydrogen absorbed in microstructure's traps caused significant degradation of mechanical properties related to ductility. Currentless charging with hydrogen in NACE-solution saturated with H2S gave the insight in stepwise morphology of cracks induced by Habs. Fractographic analyses showed the different appearance of surfaces after the cracking: ductile feature characterized the uncharged material, while brittle cleavage fracture of intergranular or transgranular type prevailed after the charging with hydrogen. KEY WORDS low alloy steel, hydrogen embrittlement, mechanical properties, stepwise cracking |